Wet flue gas desulfurization (WFGD) is the dominant technology among all kinds of technologies of FGD of coal-fired power plants in the world. The flue gas is highly corrosive after WFGD and thus may cause serious corrosion of equipment. Corrosion environment, corrosion mechanism and corrosion characteristics of the stack after WFGD are described. The research progress in controlling methods and materials for the corrosion of the stack after WFGD at home and abroad is summarized , which provides reference to solve the problem of the stack corrosion of coal-fired power plants at home.
引用该论文:YUN Hong,XU Qun-jie,ZHAO Yu-zeng,SHI Shi-feng. Research Progress in Corrosion and Protection of Stack in Wet Flue Gas Desulfurization System of Power Plants[J]. Corrosion & Protection, 2011, 32(4): 321
【1】Zhao Y, Wang S X, Chris P Nielsen, et al. Establishment of a database of emission factors for atmospheric pollutants from Chinese coal-fired power plants[J]. Atmospheric Environment, 2010, 44(12):1515-1523.
【2】Sun Z W, Wang S W, Zhou Q L, et al. Experimental study on desulfurization efficiency and gas-liquid mass transfer in a new liquid-screen desulfurization system[J]. Applied Energy, 2010, 87(5):1505-1512.
【4】Zhao Y, Wang S X, Duan L, et al. Primary air pollutant emissions of coal-red power plants in China: Current status and future prediction[J]. Atmospheric Environment, 2008, 42: 8442-8452.
【6】Le D P, Ji W S, Kim J G, et al. Effect of antimony on the corrosion behavior of low-alloy steel for flue gas desulfurization system[J]. Corrosion Science, 2008, 50(4):1195-1204.
【7】Zhong Y, Gao X, Huo W, et al. A model for performance optimization of wet flue gas desulfurization systems of power plants[J]. Fuel Processing Technology, 2008, 89(11):1025-1032.
【8】Dou B L, Pan W G, Jin Q, et al. Prediction of SO2 removal efficiency for wet flue gas desulfurization[J]. Energy Conversion and Management, 2009, 50(10):2547-2553.
【9】Barry C Syrett. Corrosion control in electric power plants-success stories[J]. Corrosion Science, 1993, 35(5/8):1189-1198.
【13】Kim M T, Chang S Y, Oh O Y, et al. Failure analysis of enamel-coated carbon steel heating elements of gas-gas heater for flue gas desulfurization system[J]. Engineering Failure Analysis, 2007, 14(4):686-693.
【20】Myers T J, Kytmaa H K, Smith T R. Environmental stress-corrosion cracking of fiberglass: Lessons learned from failures in the chemical industry[J]. Journal of Hazardous Materials, 2007, 142(3): 695-704.
【21】Liu T, Wang S, Chen G. Immobilization of trypsin on silica-coated fiberglass core in microchip for highly efficient proteolysis[J]. Talanta, 2009, 77(5):1767-1773.
【22】Antonio F, Maria Gabriela R C, Eder C D, et al. Nano-structured sandwich composites response to low-velocity impact[J]. Composite Structures, 2010, 92(3):745-751.
【23】Nilanjan M. A methodology for improving shear performance of marine grade sandwich composites: Sandwich composite panel with shear key[J]. Composite Structures, 2010, 92(5):1065-1072.
【24】Barjasteh E, Bosze E J, Tsai Y I, et al. Thermal aging of fiberglass/carbon-fiber hybrid composites[J]. Composites Part A: Applied Science and Manufacturing, 2009, 40(12):2038-2045.
【25】Sathiyanarayanan S, Azim S S, Venkatachari G. Corrosion protection coating containing polyaniline glass flake composite for steel[J]. Electrochimica Acta, 2008, 53(5):2087-2094.
【26】González-Guzmán J, Santana J J, González S, et al. Resistance of metallic substrates protected by an organic coating containing glass flakes[J]. Progress in Organic Coatings, 2010, 68(3): 240-243.
【28】Santana J J, González-Guzmán J, Fernández-Mérida L, et al. Visualization of local degradation processes in coated metals by means of scanning electrochemical microscopy in the redox competition mode[J]. Electrochimica Acta, 2010, 55(15):4488-4494.
【30】Broughton W R, Lodeiro M J, Pilkington G D. Influence of coupling agents on material behaviour of glass flake reinforced polypropylene[J]. Composites Part A: Applied Science and Manufacturing, 2010, 41(4):506-514.